Ultramid® D3WG12 HMG BK00102
聚酰胺，未指定（尼龙，未指定)
德国巴斯夫-BASF Corporation
产品说明:
Ultramid D3WG12 HMG BK00102 is a 60% glass reinforced, injection molding polyamide offering high strength and stiffness. Due to inherently lower moisture absorption, Ultramid D3WG12 HMG BK00102 shows improved retention of mechanical properties after moisture conditioning. In addition, molded parts possess an exceptional surface finish.
Applications
Ultramid D3WG12 HMG BK00102 was designed for applications requiring very high rigidity and should be considered for components that are constructed with metal.
增强材料：玻璃纤维60%增强
材料特性：出色的外观，高刚性，高强度
材料用途：金属取代
加工方法：黑色粒子注射成型
供货地区：北美洲，亚太地区
中国代理：苏州希普能工程塑料
Ultramid® D3WG12 HMG BK00102 巴斯夫中文加工参数表
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.75 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直 | 0.25 | -- | % | |
| 流动 | 0.19 | -- | % | |
| 吸水率 | ISO 62 | |||
| 饱和,23℃ | 2.5 | -- | % | |
| 平衡,23℃,50% RH | 1.0 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 20200 | 20800 | MPa | ISO 527-1 |
| 拉伸应力(断裂,23℃) | 248 | 220 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 2.5 | 2.2 | % | ISO 527-2 |
| 弯曲模量(23℃) | 18900 | 19400 | MPa | ISO 178 |
| 弯曲应力(23℃) | 383 | 351 | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30℃ | 12 | 12 | kJ/m² | |
| 23℃ | 13 | 15 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | |||
| -30℃ | 95 | 85 | kJ/m² | |
| 23℃ | 99 | 93 | kJ/m² | |
| 悬壁梁缺口冲击强度 | ISO 180 | |||
| -40℃ | 12 | 11 | kJ/m² | |
| 23℃ | 13 | 13 | kJ/m² | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 224 | -- | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 260 | -- | ℃ | ISO 3146 |
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 80 | ℃ | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.15 | % | ||
| 加工（熔体）温度 | 280 到 305 | ℃ | ||
| 模具温度 | 80 到 90 | ℃ | ||
| 注塑压力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||