Ultramid® Advanced T1000 HG7 BK23593
聚酰胺 6T/6I（尼龙 6T/6I）PA6T
德国巴斯夫-BASF Corporation
产品说明:
Preliminary Product - Ultramid Advanced T1000 HG7 BK23593 is a heat stabilized, partially aromatic, 35% glassfiber reinforced polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures and excellent chemical resistance for highly stressed parts. This material has high strength and stiffness, very low water absorption and outstanding dimensional stability. It features a high melting point (320C) and excellent melt stability.
黄卡号码：E41871-104037816
增强材料：玻璃纤维35%增强
含添加剂：热稳定剂
材料特性：芳香、高刚性、高强度、较高的熔体稳定性、耐化学品性良好、热稳定、吸水低或不吸水、High Dimensional Stability
加工方法：粒子注射成型
供货地区：欧洲、北美洲
中国代理：苏州希普能工程塑料
Ultramid® Advanced T1000 HG7 BK23593 加工参数表
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.49 | -- | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | |||
| 垂直 | 0.93 | -- | % | |
| 流动 | 0.40 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 | ISO 527-1 | |||
| 23℃ | 14000 | 14000 | MPa | |
| 80℃ | 12500 | 12000 | MPa | |
| 120℃ | 10000 | -- | MPa | |
| 拉伸应力 | ISO 527-2 | |||
| 断裂,23℃ | 220 | 210 | MPa | |
| 断裂,80℃ | 180 | 145 | MPa | |
| 断裂,120℃ | 135 | -- | MPa | |
| 拉伸应变 | ISO 527-2 | |||
| 断裂,23℃ | 2.0 | 1.9 | % | |
| 断裂,80℃ | 2.0 | 2.2 | % | |
| 断裂,120℃ | 2.9 | -- | % | |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30℃ | 8.0 | -- | kJ/m² | |
| 23℃ | 8.0 | -- | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | |||
| -30℃ | 70 | -- | kJ/m² | |
| 23℃ | 70 | -- | kJ/m² | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 280 | -- | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 320 | -- | ℃ | ISO 3146 |
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 - 热风干燥机 | 120 | ℃ | ||
| 干燥时间 | 8.0 | hr | ||
| 建议的最大水分含量 | 0.050 | % | ||
| 加工（熔体）温度 | 345 到 360 | ℃ | ||
| 模具温度 | 150 到 170 | ℃ | ||