Ultramid® B3WG10 BK00564
聚酰胺6（尼龙6）PA6
德国巴斯夫-BASF Corporation
产品说明:
This resin is a heat stabilized, 50% glass fiber reinforced PA6 injection molding compound offering excellent strength, stiffness, high temperature performance and dimensional stability. It is available in natural, black weather resistant and pigmented versions.
Applications
Ultramid B3WG10 BK00564 is generally recommended for applications such as power tool housings, cattle ear taggers, luggage frames, fans and pressure regulator housings.
含添加剂：热稳定剂
增强材料：玻璃纤维50%增强
材料特性：高刚性、高强度、高耐热、耐油、热稳定、High Dimensional Stability
材料用途：动力/其它工具、模塑耳标、皮箱、外壳
加工方法：黑色和自然色粒子注射成型
供货地区：北美洲、欧洲、亚太地区
中国代理：苏州希普能工程塑料
Ultramid® B3WG10 BK00564 巴斯夫中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.56 | g/cm³ | ISO 1183 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 4.8 | % | |
| 平衡,23℃,50% RH | 1.4 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 16700 | MPa | ISO 527-1 |
| 拉伸应力(断裂,23℃) | 225 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 2.5 | % | ISO 527-2 |
| 弯曲模量(23℃) | 14500 | MPa | ISO 178 |
| 弯曲应力(23℃) | 345 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 15 | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度(23℃) | 90 | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 | ISO 180 | ||
| -40℃ | 12 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火 | 220 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 215 | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 220 | ℃ | ISO 3146 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.060 | % | |
| 加工（熔体）温度 | 280 到 305 | ℃ | |
| 模具温度 | 80 到 95 | ℃ | |
| 注塑压力 | 3.45 到 10.3 | MPa | |
| 注射速度 | 快速 | ||