Ultramid® B3W BK102
聚酰胺6（尼龙6）PA6
德国巴斯夫-BASF Corporation
产品说明:
Ultramid B3W BK102 is an unreinforced, heat stabilized, pigmented black, low viscosity, general purpose injection molding PA6 exhibiting excellent fluidity for filling thin sections. It possesses the combination of strength, stiffness and toughness properties as well as excellent chemical, thermal and abrasion resistance. The heat stabilizer system extends its retention of properties at elevated temperatures.
Applications
Ultramid B3W BK102 is generally recommended for applications such as drapery hardware, gears, fittings, furniture casters, bearings, handles, clips and fasteners.
含添加剂：热稳定剂
材料特性：低粘度、良好的强度、良好刚性、流动性高、热稳定、韧性良好
材料用途：把手、齿轮、轴承
加工方法：黑色粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultramid® B3W BK102 巴斯夫中文加工参数表
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 | 1.13 | -- | g/cm³ | ISO 1183 |
| 吸水率 | ISO 62 | |||
| 24 hr,23℃ | 1.6 | -- | % | |
| 饱和,23℃ | 9.5 | -- | % | |
| 平衡,23℃,50% RH | 2.7 | -- | % | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 3100 | 970 | MPa | ISO 527-1 |
| 拉伸应力(屈服,23℃) | 85.0 | 36.0 | MPa | ISO 527-2 |
| 拉伸应变(屈服,23℃) | 4.0 | 16 | % | ISO 527-2 |
| 标称拉伸断裂应变(23℃) | 25 | > 50 | % | ISO 527-2 |
| 弯曲模量(23℃) | 2650 | 770 | MPa | ISO 178 |
| 弯曲应力(23℃) | 90.0 | 25.0 | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 3.0 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度(23℃) | 无断裂 | -- | ISO 179 | |
| 悬壁梁缺口冲击强度 | ISO 180 | |||
| -40℃ | 4.0 | -- | kJ/m² | |
| 23℃ | 5.5 | -- | kJ/m² | |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 60.0 | -- | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 220 | -- | ℃ | ISO 3146 |
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 80 | ℃ | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.15 | % | ||
| 加工（熔体）温度 | 240 到 285 | ℃ | ||
| 模具温度 | 65 到 80 | ℃ | ||
| 注塑压力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||