Ultramid® B3WM8 BK00102
聚酰胺6（尼龙6）PA6
德国巴斯夫-BASF Corporation
产品说明:
Ultramid B3WM8 BK00102 is a heat stabilized, pigmented black, 40% mineral reinforced PA6 injection molding resin. It possesses high stiffness, dimensional stability and heat resistance combined with excellent processability including low warp and resistance to sink-mark formation. It maintains its inherent chemical resistance to greases, oils and hydrocarbons.
Applications
Ultramid B3WM8 BK00102 is generally recommended for applications such as marine hardware, brackets, fittings, bobbins, office furniture, appliance components, and power tool housings.
增强材料：矿物40%填充
含添加剂：热稳定剂
材料特性：低翘曲、高刚性、耐化学品良好、高耐热、耐碳氢化合物、耐油脂、优异的加工性能、High Dimensional Stability
材料用途：船舶应用、动力/其它工具、家电部件、家具、配件、外壳、线轴
加工方法：黑色粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultramid® B3WM8 BK00102巴斯夫中文加工参数表
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度/比重 | 1.49 | -- | g/cm³ | ASTM D792,ISO 1183 |
| 吸水率 | ||||
| 24 hr | 1.1 | -- | % | ASTM D570 |
| 24 hr,23℃ | 1.1 | -- | % | ISO 62 |
| 饱和 | 5.7 | -- | % | ASTM D570 |
| 饱和,23℃ | 5.7 | -- | % | ISO 62 |
| 平衡,50% RH | 1.6 | -- | % | ASTM D570 |
| 平衡,23℃,50% RH | 1.6 | -- | % | ISO 62 |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 | ISO 527-1 | |||
| -40℃ | 8310 | 7700 | MPa | |
| 23℃ | 6400 | 3800 | MPa | |
| 80℃ | 1360 | 1400 | MPa | |
| 120℃ | 970 | 1200 | MPa | |
| 150℃ | 910 | 840 | MPa | |
| 拉伸应力 | ISO 527-2 | |||
| 断裂,-40℃ | 135 | 135 | MPa | |
| 断裂,23℃ | 85.0 | 60.0 | MPa | |
| 断裂,80℃ | 40.0 | 35.0 | MPa | |
| 断裂,120℃ | 30.0 | 27.0 | MPa | |
| 断裂,150℃ | 20.0 | 20.0 | MPa | |
| 拉伸应变 | ISO 527-2 | |||
| 断裂,-40℃ | 6.0 | 5.0 | % | |
| 断裂,23℃ | 10 | 30 | % | |
| 断裂,80℃ | 35 | 30 | % | |
| 断裂,120℃ | 40 | 40 | % | |
| 断裂,150℃ | 40 | 60 | % | |
| 弯曲模量(23℃) | 5200 | 2100 | MPa | ISO 178 |
| 弯曲应力(23℃) | 140 | 50.0 | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 3.0 | -- | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度(23℃) | 130 | -- | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度(23℃) | 6.0 | -- | kJ/m² | ISO 180 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 载荷下热变形温度 | ||||
| 0.45 MPa,未退火 | 190 | -- | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 90.0 | -- | ℃ | ISO 75-2/A |
| 熔融峰值温度 | 220 | -- | ℃ | ASTM D3418,ISO 3146 |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率 | ||||
| 1.50 mm | > 1.0E+15 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 83 | ℃ | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.15 | % | ||
| 加工（熔体）温度 | 270 到 295 | ℃ | ||
| 模具温度 | 80 到 95 | ℃ | ||
| 注塑压力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||