SABIC VALOX™ T3N8032UX
聚对苯二甲酸丁二酯 + PET (PBT+PET)
VALOX™ RESIN T3N8032UX is a ETP compound, which is formulated with 34wt% post-industrial recycled plastics.
The grade is part of SABIC’s TRUCIRCLE™ portfolio and services.
VALOX™ RESIN T3N8032UX is a 30% glass fibre reinforced, UV stabilized PBT+PET blend with excellent surface finish. This grade is VALOX T3N8032U with improved weathering resistance. Applications: appliance housings, door handles, mirror brackets.
回收含量：Post-Industrial (PIR)/Pre-Consumer, 34%
材料特性：抗紫外线
材料用途：电器外壳，门把手，镜子支架
供货地区：欧洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.57 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 265℃/2.16 kg | 21 | g/10 min | |
| 265℃/5.0 kg | 45 | g/10 min | |
| 熔融体积流量（MVR） | ISO 1133 | ||
| 250℃/5.0 kg | 20 | cm³/10min | |
| 265℃/2.16 kg | 15 | cm³/10min | |
| 265℃/5.0 kg | 35 | cm³/10min | |
| 收缩率 | |||
| 流动:24小时 | 0.10 到 0.50 | % | ASTM D955,ISO 294-4 |
| 横向流动:24小时 | 0.60 到 1.0 | % | ASTM D955 |
| 垂直:24小时 | 0.60 到 1.0 | % | ISO 294-4 |
| 吸水率 | |||
| 24 hr,23℃ | 0.070 | % | ASTM D570 |
| 24 hr,23℃,50% RH | 0.050 | % | ASTM D570 |
| 饱和,23℃ | 0.22 | % | ISO 62 |
| 平衡,23℃,50% RH | 0.070 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --2 | 10500 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服3 | 140 | MPa | ASTM D638 |
| 屈服 | 145 | MPa | ISO 527-2/5 |
| 断裂3 | 140 | MPa | ASTM D638 |
| 断裂 | 145 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服3 | 2.5 | % | ASTM D638 |
| 屈服 | 2.5 | % | ISO 527-2/5 |
| 断裂3 | 2.5 | % | ASTM D638 |
| 断裂 | 2.5 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距4 | 9500 | MPa | ASTM D790 |
| --5 | 9500 | MPa | ISO 178 |
| 弯曲应力 | |||
| --5,6 | 210 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距4 | 205 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距4 | 200 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles,1000g,CS-17 转轮) | 30.0 | mg | 内部方法 |
| 弯曲应变 - at Break7 | 3.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度8 | ISO 179/1eA,ISO 179/2C | ||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 9.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | |||
| -30℃8 | 40 | kJ/m² | ISO 179/1eU |
| -30℃ | 50 | kJ/m² | ISO 179/2U |
| 23℃8 | 45 | kJ/m² | ISO 179/1eU |
| 23℃ | 58 | kJ/m² | ISO 179/2U |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 65 | J/m | ASTM D256 |
| 23℃ | 70 | J/m | ASTM D256 |
| -30℃9 | 8.0 | kJ/m² | ISO 180/1A |
| 0℃9 | 8.0 | kJ/m² | ISO 180/1A |
| 23℃9 | 9.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -30℃ | 700 | J/m | ASTM D4812 |
| 23℃ | 750 | J/m | ASTM D4812 |
| -30℃9 | 45 | kJ/m² | ISO 180/1U |
| 23℃9 | 50 | kJ/m² | ISO 180/1U |
| 装有测量仪表的落镖冲击(23℃,Total Energy) | 8.00 | J | ASTM D3763 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 120 | ISO 2039-2 | |
| 球压硬度(H 358/30) | 234 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 220 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 220 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 200 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 200 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 220 | ℃ | ASTM D152510,ISO 306/A5010 |
| -- | 210 | ℃ | ASTM D152511,ISO306/B120,ISO306/B50 |
| Ball Pressure Test(123 到 127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动:-40 到 40℃ | 2.5E-5 | cm/cm/℃ | ASTM E831 |
| 流动:23 到 60℃ | 2.2E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 7.5E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:23 到 60℃ | 1.0E-4 | cm/cm/℃ | ISO 11359-2 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+15 | ohms·cm | IEC 60093 |
| 介电强度 | IEC 60243-1 | ||
| 0.800 mm,在油中 | 27 | kV/mm | |
| 1.60 mm,在油中 | 23 | kV/mm | |
| 3.20 mm,在油中 | 15 | kV/mm | |
| 相对电容率 | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 100 Hz | 3.60 | ||
| 1 MHz | 3.20 | ||
| 耗散因数 | IEC 60250 | ||
| 50 Hz | 8.0E-4 | ||
| 60 Hz | 8.0E-4 | ||
| 1 MHz | 0.013 | ||
| 相比耐漏电起痕指数(CTI) | PLC 2 | UL 746A | |
| 漏电起痕指数 | 300 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级(1.6 mm,Testing by SABIC) | HB | UL 94 | |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 195 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 30 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 240 到 260 | ℃ | |
| 料筒中部温度 | 255 到 280 | ℃ | |
| 料筒前部温度 | 260 到 280 | ℃ | |
| 射嘴温度 | 265 到 275 | ℃ | |
| 加工（熔体）温度 | 260 到 285 | ℃ | |
| 模具温度 | 60 到 110 | ℃ | |
| 备注 1一般属性：这些不能被视为规格。 25.0 mm/min 3类型 1,5.0 mm/min 41.3 mm/min 52.0 mm/min 6at Yield 72 mm/min 880*10*4 sp=62mm 980*10*4 mm 10速率 A (50℃/h),压力1 (10N) 11速率 A (50℃/h),载荷2 (50N) |
|||