SABIC VALOX™ T1N830
聚丁烯对苯二甲酸酯(PBT)
VALOX™ RESIN T1N830 is a ETP compound, which is formulated with 15wt% post-industrial recycled plastics.
The grade is part of SABIC’s TRUCIRCLE™ portfolio and services.
VALOX™ RESIN T1N830 is a 30% GR PBTP compound with excellent surface finish. Typical applications are hot air gun housing assemblies, industrial glue guns, appliance housings and handles.
回收含量：Post-Industrial (PIR)/Pre-Consumer, 15%
材料用途：热风枪外壳组件、工业胶枪、电器外壳和手柄
供货地区：欧洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | |||
| -- | 1.54 | g/cm³ | ASTM D792 |
| -- | 1.55 | g/cm³ | ISO 1183 |
| 熔流率（熔体流动速率） | ASTM D1238 | ||
| 265℃/2.16 kg | 16 | g/10 min | |
| 265℃/5.0 kg | 45 | g/10 min | |
| 熔融体积流量（MVR） | ISO 1133 | ||
| 250℃/5.0 kg | 23 | cm³/10min | |
| 265℃/2.16 kg | 14 | cm³/10min | |
| 265℃/5.0 kg | 35 | cm³/10min | |
| 收缩率 | 内部方法 | ||
| 垂直2 | 0.60 到 1.0 | % | |
| 流动2 | 0.40 到 0.80 | % | |
| 流动:3.20 mm | 0.20 到 1.0 | % | |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.15 | % | |
| 平衡,23℃,50% RH | 0.060 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --3 | 10500 | MPa | ASTM D638 |
| -- | 10500 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服4 | 140 | MPa | ASTM D638 |
| 屈服 | 140 | MPa | ISO 527-2/5 |
| 断裂4 | 140 | MPa | ASTM D638 |
| 断裂 | 140 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服4 | 3.0 | % | ASTM D638 |
| 屈服 | 3.0 | % | ISO 527-2/5 |
| 断裂4 | 3.0 | % | ASTM D638 |
| 断裂 | 3.0 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距5 | 7000 | MPa | ASTM D790 |
| --6 | 8800 | MPa | ISO 178 |
| 弯曲应力 | |||
| --6,7 | 215 | MPa | ISO 178 |
| --6,8 | 200 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距5 | 205 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距5 | 205 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles,1000g,CS-17 转轮) | 30.0 | mg | 内部方法 |
| 弯曲应变 - at Break9 | 3.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | |||
| -30℃10 | 9.0 | kJ/m² | ISO 179/1eA |
| -30℃ | 10 | kJ/m² | ISO 179/2C |
| 23℃10 | 9.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 10 | kJ/m² | ISO 179/2C |
| 简支梁无缺口冲击强度 | |||
| -30℃10 | 50 | kJ/m² | ISO 179/1eU |
| -30℃ | 55 | kJ/m² | ISO 179/2U |
| 23℃10 | 60 | kJ/m² | ISO 179/1eU,ISO 179/2U |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 90 | J/m | ASTM D256 |
| 0℃ | 90 | J/m | ASTM D256 |
| 23℃ | 85 | J/m | ASTM D256 |
| -30℃11 | 9.0 | kJ/m² | ISO 180/1A |
| 0℃11 | 9.0 | kJ/m² | ISO 180/1A |
| 23℃11 | 10 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -30℃ | 800 | J/m | ASTM D4812 |
| 23℃ | 800 | J/m | ASTM D4812 |
| -30℃11 | 50 | kJ/m² | ISO 180/1U |
| 23℃11 | 50 | kJ/m² | ISO 180/1U |
| 装有测量仪表的落镖冲击(23℃,Total Energy) | 3.00 | J | ASTM D3763 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 123 | ISO 2039-2 | |
| 球压硬度(H358/30) | 174 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 220 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,100 mm 跨距12 | 220 | ℃ | ISO 75-2/Be |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距11 | 220 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 200 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,6.40 mm | 208 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,100 mm 跨距12 | 202 | ℃ | ISO 75-2/Ae |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距11 | 200 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 220 | ℃ | ASTM D152513,ISO 306/A5013 |
| -- | 208 | ℃ | ASTM D152514,ISO 306/B120,ISO 306/B50 |
| Ball Pressure Test(123 到127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动:-40 到 40℃ | 2.7E-5 | cm/cm/℃ | ASTM E831 |
| 流动:-40 到 40℃ | 2.0E-5 | cm/cm/℃ | ISO 11359-2 |
| 流动:23 到 80℃ | 2.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 流动:23 到 150℃ | 1.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 7.8E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:-40 到 40℃ | 6.6E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:23 到 80℃ | 8.1E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:23 到 150℃ | 1.4E-5 | cm/cm/℃ | ISO 11359-2 |
| RTI Elec | 120 | ℃ | UL 746B |
| RTI | 120 | ℃ | UL 746B |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介电强度 | |||
| 0.800 mm,in Oil | 27 | kV/mm | ASTM D149 |
| 1.60 mm,in Oil | 23 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 15 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 27 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 23 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 15 | kV/mm | IEC 60243-1 |
| 介电常数 | |||
| 1 MHz | 3.20 | ASTM D150 | |
| 50 Hz | 3.30 | IEC 60250 | |
| 60 Hz | 3.30 | IEC 60250 | |
| 100 Hz | 3.60 | IEC 60250 | |
| 1 MHz | 3.50 | IEC 60250 | |
| 耗散因数 | |||
| 1 MHz | 0.013 | ASTM D150,IEC 60250 | |
| 50 Hz | 8.0E-4 | IEC 60250 | |
| 60 Hz | 8.0E-4 | IEC 60250 | |
| 100 Hz | 2.0E-3 | IEC 60250 | |
| 耐电弧性15 | PLC 6 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 2 | UL 746A | |
| 漏电起痕指数 | IEC 60112 | ||
| -- | 325 | V | |
| 解决方案 B | 150 | V | |
| 高电弧燃烧指数(HAI)16 | PLC 3 | UL 746A | |
| 高压电弧抗点燃指数 (HVAR) (PLC) | PLC 2 | UL 746A | |
| 热丝引燃 (HWI) | PLC 0 | UL 746A | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 1.5 mm,Testing by SABIC | HB | ||
| 3.0 mm,Testing by SABIC | HB | ||
| 灼热丝易燃指数(1.0 mm) | 750 | ℃ | IEC 60695-2-12 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 208 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 30 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 240 到 260 | ℃ | |
| 料筒中部温度 | 255 到 280 | ℃ | |
| 料筒前部温度 | 260 到 280 | ℃ | |
| 射嘴温度 | 265 到 275 | ℃ | |
| 加工（熔体）温度 | 260 到 285 | ℃ | |
| 模具温度 | 60 到 110 | ℃ | |
| 备注 1一般属性：这些不能被视为规格。 2Tensile Bar 35.0 mm/min 4类型 1, 5.0 mm/min 51.3 mm/min 62.0 mm/min 7at Yield 8at Break 92 mm/min 1080*10*4 sp=62mm 1180*10*4 mm 12120*10*4 mm 13速率 A (50℃/h), 压 力1 (10N) 14速率 A (50℃/h), 载荷2 (50N) 15钨电极 16Surface |
|||