VALOX™ ENH8530
Generic Name: 聚对苯二甲酸丁二酯 + PET (PBT+PET) - 提供方: SABIC
VALOX ENH8530 is a 15% glass reinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate/Polyethylene Terephthalate (PBT/PET) injection moldable grade with excellent chemical resistance. It has a UL94V0@1.5mm and 5VA@2.0mm flame rating. This is a good candidate for a variety of applications needing a sustainable FR PBT/PET solution.
黄卡号码：E45329-100700420
增强材料：玻璃纤维15%增强
材料特性：耐化学品良好、无溴阻燃、Chlorine Free
外观形式：粒子注射成型
供货地区：欧洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.46 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率） | |||
| 265℃/2.16 kg | 20 | g/10 min | ASTM D1238 |
| 250℃/5.0 kg | 15 | g/10 min | ISO 1133 |
| 溶化体积流率（MVR） | |||
| 250℃/5.0 kg | 11 | cm³/10min | ASTM D1238 |
| 265℃/1.2 kg | 5.0 | cm³/10min | ISO 1133 |
| 265℃/2.16 kg | 13 | cm³/10min | ISO 1133 |
| 265℃/5.0 kg | 45 | cm³/10min | ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 7200 | MPa | ASTM D638 |
| -- | 7400 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服2 | 75.0 | MPa | ASTM D638 |
| 屈服 | 75.0 | MPa | ISO 527-2/5 |
| 断裂2 | 75.0 | MPa | ASTM D638 |
| 断裂 | 75.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服2 | 2.0 | % | ASTM D638 |
| 屈服 | 2.0 | % | ISO 527-2/5 |
| 断裂2 | 2.0 | % | ASTM D638 |
| 断裂 | 2.0 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 6000 | MPa | ASTM D790 |
| --4 | 6300 | MPa | ISO 178 |
| 弯曲应力 | |||
| --4,5 | 125 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 110 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距3 | 110 | MPa | ASTM D790 |
| 弯曲应变-at Break6 | 3.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179/2C | ||
| -30℃ | 5.0 | kJ/m² | |
| 23℃ | 5.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179/2U | ||
| -30℃ | 20 | kJ/m² | |
| 23℃ | 23 | kJ/m² | |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 45 | J/m | ASTM D256 |
| 0℃ | 45 | J/m | ASTM D256 |
| 23℃ | 45 | J/m | ASTM D256 |
| -30℃7 | 5.0 | kJ/m² | ISO 180/1A |
| 0℃7 | 5.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 5.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -30℃ | 280 | J/m | ASTM D4812 |
| 23℃ | 330 | J/m | ASTM D4812 |
| -30℃7 | 20 | kJ/m² | ISO 180/1U |
| 23℃7 | 22 | kJ/m² | ISO 180/1U |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 120 | ISO 2039-2 | |
| 球压硬度(H 358/30) | 142 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 215 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0mm 跨距7 | 215 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 190 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0mm 跨距7 | 180 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 220 | ℃ | ASTM D15258 |
| -- | 202 | ℃ | ASTM D15259 |
| -- | 200 | ℃ | ISO 306/B120 |
| -- | 196 | ℃ | ISO 306/B50 |
| -- | 215 | ℃ | ISO 306/A50 |
| Ball Pressure Test(123到127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动:-40 到 40℃ | 3.1E-5 | cm/cm/℃ | |
| 流动:23 到 150℃ | 4.6E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 6.3E-5 | cm/cm/℃ | |
| 垂直:23 到 150℃ | 1.7E-4 | cm/cm/℃ | |
| RTI Elec | 130 | ℃ | UL 746B |
| RTI Imp | 75.0 | ℃ | UL 746B |
| RTI | 130 | ℃ | UL 746B |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介电强度 | |||
| 0.800 mm,in Oil | 38 | kV/mm | ASTM D149 |
| 1.60 mm,in Oil | 28 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 19 | kV/mm | ASTM D149 |
| 0.800 mm,在油中 | 38 | kV/mm | IEC 60243-1 |
| 1.60 mm,在油中 | 28 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 19 | kV/mm | IEC 60243-1 |
| 介电常数(1 MHz) | 3.30 | ASTM D150,IEC 60250 | |
| 耗散因数(1 MHz) | 0.010 | ASTM D150,IEC 60250 | |
| 相比耐漏电起痕指数(CTI) | PLC 1 | UL 746A | |
| 漏电起痕指数10 | 400 | V | IEC 60112 |
| 高电弧燃烧指数(HAI)(> 0.8 mm) | PLC 0 | UL 746A | |
| 热丝引燃 (HWI) | UL 746A | ||
| > 0.8 mm | PLC 3 | ||
| > 1.5 mm | PLC 0 | ||
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| > 1.5 mm | V-0 | ||
| > 2.0 mm | 5VA | ||
| 灼热丝易燃指数 | IEC 60695-2-12 | ||
| 0.8 mm | 960 | ℃ | |
| 1.5 mm | 850 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 0.8 mm | 750 | ℃ | |
| 1.5 mm | 750 | ℃ | |
| 3.0 mm | 800 | ℃ | |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 145 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 15 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 4.0 到 6.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 240 到 260 | ℃ | |
| 料筒中部温度 | 255 到 280 | ℃ | |
| 料筒前部温度 | 260 到 280 | ℃ | |
| 射嘴温度 | 265 到 275 | ℃ | |
| 加工（熔体）温度 | 260 到 285 | ℃ | |
| 模具温度 | 60 到 110 | ℃ | |
| 备注 15.0 mm/min 2类型 1,5.0 mm/min 31.3 mm/min 42.0 mm/min 5at Break 62 mm/min 780*10*4 mm 8速率 A (50°C/h),压 力1 (10N) 9速率 A (50°C/h),载荷2 (50N) 10Value shown here is based on internal measurement. |
|||
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(PTA)或者对苯二甲酸酯(DMT)聚缩合而成，分子式为(C8H8·C4H6·C3H3N)x，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。