VALOX™ ENH3500
Generic Name: 聚丁烯对苯二甲酸酯(PBT) - 提供方: SABIC
VALOX ENH3500 is an unreinforced, non-chlorinated/brominated flame retardant Polybutylene Terephthalate (PBT) injection moldable grade with excellent chemical resistance. It has a UL94V0@0.80mm flame rating. This is a good candidate for a variety of applications needing a sustainable FR PBT solution.
黄卡号码：E207780-100208979
材料特性：耐化学品良好、无溴阻燃、Chlorine Free
材料用途：电气/电子应用领域、电气元件、电线电缆应用、医疗/护理用品
外观形式：粒子
供货地区：亚太地区
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.31 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融体积流量（MVR）(250℃/2.16kg) | 20 | cm³/10min | ISO 1133 |
| 收缩率-流动1 | 1.8 到 2.8 | % | 内部方法 |
| 吸水率 | |||
| 24 hr,23℃,50% RH | 0.080 | % | ASTM D570 |
| 24 hr,23℃ | 0.35 | % | ASTM D570 |
| 饱和,23℃ | 0.35 | % | ISO 62 |
| 平衡,23℃,50% RH | 0.080 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --2 | 3150 | MPa | ASTM D638 |
| -- | 3200 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服3 | 44.0 | MPa | ASTM D638 |
| 屈服 | 39.0 | MPa | ISO 527-2/50 |
| 断裂3 | 42.0 | MPa | ASTM D638 |
| 断裂 | 38.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服3 | 3.0 | % | ASTM D638 |
| 屈服 | 3.0 | % | ISO 527-2/50 |
| 断裂3 | 10 | % | ASTM D638 |
| 断裂 | 8.0 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距4 | 2750 | MPa | ASTM D790 |
| --5 | 2700 | MPa | ISO 178 |
| 弯曲应力 | |||
| --5,6 | 70.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距4 | 77.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度7(23℃) | 6.0 | kJ/m² | ISO 179/1eA |
| 简支梁无缺口冲击强度7(23℃) | 无断裂 | ISO 179/1eU | |
| 悬壁梁缺口冲击强度 | |||
| 23℃ | 40 | J/m | ASTM D256 |
| -30℃8 | 5.0 | kJ/m² | ISO 180/1A |
| 23℃8 | 5.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| 23℃ | 无断裂 | ASTM D4812,ISO 180/1U | |
| -30℃8 | 无断裂 | ISO 180/1U | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45MPa,未退火,3.20 mm | 160 | ℃ | ASTM D648 |
| 0.45MPa,未退火,4.00 mm,64.0 mm 跨距8 | 160 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 60.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距8 | 60.0 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | 170 | ℃ | ASTM D15259,ISO 306/B120,ISO 306/B50 |
| 线形热膨胀系数 | ASTM E831 | ||
| 流动:-40到95℃ | 8.0E-5 | cm/cm/℃ | |
| 垂直:-40到95℃ | 8.0E-5 | cm/cm/℃ | |
| RTI Elec | 150 | ℃ | UL 746B |
| RTI Imp | 105 | ℃ | UL 746B |
| RTI | 150 | ℃ | UL 746B |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 相比耐漏电起痕指数(CTI) | PLC 0 | UL 746A | |
| 漏电起痕指数 | 525 | V | IEC 60112 |
| 高电弧燃烧指数(HAI)(> 0.8 mm) | PLC 0 | UL 746A | |
| 热丝引燃 (HWI) | UL 746A | ||
| > 0.8mm | PLC 4 | ||
| > 1.5mm | PLC 3 | ||
| > 3.0 mm | PLC 2 | ||
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| > 0.8mm | V-0 | ||
| > 2.0mm | 5VB | ||
| > 3.0mm | 5VA | ||
| 灼热丝易燃指数 | IEC 60695-2-12 | ||
| 0.8 mm | 960 | ℃ | |
| 1.5 mm | 960 | ℃ | |
| 2.0 mm | 960 | ℃ | |
| 3.0 mm | 960 | ℃ | |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 0.8 mm | 750 | ℃ | |
| 1.5 mm | 700 | ℃ | |
| 2.0 mm | 700 | ℃ | |
| 3.0 mm | 700 | ℃ | |
| 极限氧指数 | 31 | % | ASTM D2863,ISO 4589-2 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 230 到 240 | ℃ | |
| 料筒中部温度 | 235 到 250 | ℃ | |
| 料筒前部温度 | 240 到 260 | ℃ | |
| 射嘴温度 | 230 到 255 | ℃ | |
| 加工（熔体）温度 | 245 到 260 | ℃ | |
| 模具温度 | 40 到 100 | ℃ | |
| 备注 1Tensile Bar 25.0 mm/min 3类型 1,50 mm/min 41.3 mm/min 52.0 mm/min 6at Yield 780*10*4 sp=62mm 880*10*4 mm 9速率 A (50°C/h),载荷2 (50N) |
|||
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(PTA)或者对苯二甲酸酯(DMT)聚缩合而成，分子式为(C8H8·C4H6·C3H3N)x，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。