VALOX™ 771
Generic Name: 聚丁烯对苯二甲酸酯(PBT) - 提供方: SABIC
VALOX 771 is a 35% mineral/glass filled, flame retardant Polybutylene Terephthalate (PBT) injection moldable grade. It has excellent chemical resistance and a UL94V0@0.75 flame rating and 5VA@2.0mm. This grade also has a CTI of 0 and is a good candidate for applications that may see electrical arcing.
黄卡号码：E45329-236615
材料用途：Water Management、电气/电子应用领域、电气元件、电器用具、电子显示器
供货地区：欧洲
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.70 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(266℃/5.0 kg) | 20 | g/10 min | ASTM D1238 |
| 熔融体积流量（MVR） | ISO 1133 | ||
| 250℃/5.0 kg | 8.0 | cm³/10min | |
| 265℃/5.0 kg | 16 | cm³/10min | |
| 收缩率1 | 内部方法 | ||
| 垂直 | 0.40 到 1.0 | % | |
| 流动 | 0.30 到 0.60 | % | |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.94 | % | |
| 平衡,23℃,50% RH | 0.090 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --2 | 9500 | MPa | ASTM D638 |
| -- | 9700 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服3 | 85.0 | MPa | ASTM D638 |
| 屈服 | 85.0 | MPa | ISO 527-2/5 |
| 断裂3 | 85.0 | MPa | ASTM D638 |
| 断裂 | 85.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服3 | 2.0 | % | ASTM D638 |
| 屈服 | 2.0 | % | ISO 527-2/5 |
| 断裂3 | 2.0 | % | ASTM D638 |
| 断裂 | 2.0 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距4 | 7900 | MPa | ASTM D790 |
| --5 | 8400 | MPa | ISO 178 |
| 弯曲应力 | |||
| --5,6 | 120 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距4 | 110 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距4 | 110 | MPa | ASTM D790 |
| 泰伯耐磨性(1000 Cycles,1000 g,CS-17 转轮) | 55.0 | mg | 内部方法 |
| 弯曲应变-at Break7 | 2.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | |||
| -30℃8 | 4.0 | kJ/m² | ISO 179/1eA |
| -30℃ | 6.0 | kJ/m² | ISO 179/2C |
| 23℃8 | 4.0 | kJ/m² | ISO 179/1eA |
| 23℃ | 6.0 | kJ/m² | ISO 179/2C |
| 简支梁无缺口冲击强度 | |||
| -30℃8 | 20 | kJ/m² | ISO 179/1eU |
| -30℃ | 29 | kJ/m² | ISO 179/2U |
| 23℃8 | 45 | kJ/m² | ISO 179/1eU |
| 23℃ | 29 | kJ/m² | ISO 179/2U |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 51 | J/m | ASTM D256 |
| 0℃ | 52 | J/m | ASTM D256 |
| 23℃ | 52 | J/m | ASTM D256 |
| -30℃9 | 5.0 | kJ/m² | ISO 180/1A |
| 0℃9 | 5.0 | kJ/m² | ISO 180/1A |
| 23℃9 | 5.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -30℃ | 390 | J/m | ASTM D4812 |
| 23℃ | 390 | J/m | ASTM D4812 |
| -30℃9 | 25 | kJ/m² | ISO 180/1U |
| 23℃9 | 25 | kJ/m² | ISO 180/1U |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 111 | ISO 2039-2 | |
| 球压硬度(H 358/30) | 120 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 220 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,100 mm 跨距10 | 215 | ℃ | ISO 75-2/Be |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 220 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 203 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,100 mm 跨距10 | 190 | ℃ | ISO 75-2/Ae |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距9 | 190 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 220 | ℃ | ASTM D152511,ISO 306/A5011 |
| -- | 190 | ℃ | ASTM D152512,ISO 306/B120,ISO 306/B50 |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 123 到 127℃ | 通过 | ||
| 173 到 177℃ | 通过 | ||
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动:-40 到 40℃ | 2.3E-5 | cm/cm/℃ | |
| 流动:23 到 80℃ | 3.0E-5 | cm/cm/℃ | |
| 流动:23 到 150℃ | 3.0E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 5.9E-5 | cm/cm/℃ | |
| 垂直:23 到 80℃ | 9.5E-5 | cm/cm/℃ | |
| 垂直:23 到 150℃ | 1.4E-4 | cm/cm/℃ | |
| RTI Elec | 120 | ℃ | UL 746B |
| RTI Imp | 125 | ℃ | UL 746B |
| RTI | 140 | ℃ | UL 746B |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介电强度 | IEC 60243-1 | ||
| 1.60 mm,在油中 | 23 | kV/mm | |
| 3.20 mm,在油中 | 20 | kV/mm | |
| 相对电容率 | IEC 60250 | ||
| 50 Hz | 3.30 | ||
| 60 Hz | 3.30 | ||
| 1 MHz | 3.10 | ||
| 耗散因数 | IEC 60250 | ||
| 50 Hz | 9.5E-3 | ||
| 60 Hz | 9.5E-3 | ||
| 1 MHz | 0.013 | ||
| 耐电弧性13 | PLC 4 | ASTM D495 | |
| 相比耐漏电起痕指数(CTI) | PLC 0 | UL 746A | |
| 漏电起痕指数 | IEC 60112 | ||
| -- | 600 | V | |
| 解决方案 B | 175 | V | |
| 高电弧燃烧指数(HAI)14 | PLC 0 | UL 746A | |
| 高压电弧抗点燃指数 (HVAR) (PLC) | PLC 0 | UL 746A | |
| 热丝引燃 (HWI) | PLC 0 | UL 746A | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.62 mm | V-2 | ||
| 0.75 mm | V-0 | ||
| 2.0 mm | 5VA | ||
| 灼热丝易燃指数(1.0 mm) | 960 | ℃ | IEC 60695-2-12 |
| 热灯丝点火温度 | IEC 60695-2-13 | ||
| 1.0 mm | 675 | ℃ | |
| 1.5 mm | 675 | ℃ | |
| 2.0 mm | 675 | ℃ | |
| 3.0 mm | 775 | ℃ | |
| 极限氧指数 | 31 | % | ISO 4589-2 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 140 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 35 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 245 到 255 | ℃ | |
| 料筒中部温度 | 250 到 260 | ℃ | |
| 料筒前部温度 | 255 到 265 | ℃ | |
| 射嘴温度 | 255 到 275 | ℃ | |
| 加工（熔体）温度 | 255 到 275 | ℃ | |
| 模具温度 | 40 到 100 | ℃ | |
| 备注 1Tensile Bar 25.0 mm/min 3类型 1,5.0 mm/min 41.3 mm/min 52.0 mm/min 6at Yield 72 mm/min 880*10*4 sp=62mm 980*10*4 mm 10120*10*4 mm 11速率 A (50°C/h),压 力1 (10N) 12速率 A (50°C/h),载荷2 (50N) 13钨电极 14Surface |
|||
聚对苯二甲酸丁二醇酯，英文名polybutylene terephthalate（简称PBT），属于聚酯系列，是由1.4-pbt丁二醇(1.4-Butylene glycol)与对苯二甲酸(PTA)或者对苯二甲酸酯(DMT)聚缩合而成，分子式为(C8H8·C4H6·C3H3N)x，并经由混炼程序制成的乳白色半透明到不透明、结晶型热塑性聚酯树脂。与PET一起统称为热塑性聚酯，或饱和聚酯。PBT是最坚韧的工程热塑材料之一，它是半结晶材料，有非常好的化学稳定性、机械强度、电绝缘特性和热稳定性。