Ultradur® B 4040 G3 FR BK5830 Q605
聚对苯二甲酸丁二酯+PET (PBT+PET)
德国巴斯夫-BASF Corporation
产品说明:
Ultradur B 4040 G3 FR BK5830 Q605 is a 15% glass filled, pigmented black, injection molding, flame retarded PBT+PET product. The product is intended for household appliances where good chemical resistance, heat resistance and flame retardancy are required. The product also exhibits good surface appearance.
Applications
Applications include oven and range top components, exterior parts for deep fryers, toasters, coffee machines, steam irons and cooker knobs and handles.
黄卡号码：E36632-100851202
增强材料：玻璃纤维15%增强
材料特性：耐化学品良好，耐热良好，优良外观，阻燃
材料用途：电器用具
加工方法：黑色粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultradur® B 4040 G3 FR BK5830 Q605 巴斯夫中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.56 | g/cm³ | ISO 1183 |
| 熔融体积流量（MVR）(265℃/2.16kg) | 36 | cm³/10min | ISO 1133 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸应力(断裂,23℃) | 90.0 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 1.7 | % | ISO 527-2 |
| 弯曲模量(23℃) | 6080 | MPa | ISO 178 |
| 弯曲应力(23℃) | 139 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度(23℃) | 4.7 | kJ/m² | ISO 179 |
| 简支梁无缺口冲击强度(23℃) | 23 | kJ/m² | ISO 179 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 溶融温度（DSC） | 223 | ℃ | ISO 3146 |
| RTI Elec | UL 746B | ||
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ | |
| RTI Imp | UL 746B | ||
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI | UL 746B | ||
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 1.5 mm | V-0 | ||
| 5VA | |||
| 3.0 mm | V-0 | ||
| 5VA | |||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 100 到 120 | ℃ | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.015 | % | |
| 加工（熔体）温度 | 240 到 275 | ℃ | |
| 模具温度 | 60 到 100 | ℃ | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | < 1.00 | MPa | |