Ultramid® A3WG6 BK00564
聚酰胺 66 （尼龙66）PA66
德国巴斯夫-BASF Corporation
产品说明:
Ultramid A3WG6 BK00564 is a 30% glass fiber reinforced, pigmented black and heat resistance injection molding PA66 grade for machinery components and housings of high stiffness and dimensional stability. A3EG6 is the preferred grade for producing electrically insulating parts.
Applications
Typical applications include lamp socket housings, cooling fans, insulating profiles for aluminum window frames, water containers for automotive cooling systems.
黄卡号码：E36632-531632、E41871-233745、E41871-101468834
增强材料：玻璃纤维30%增强
材料特性：高刚性、耐热良好、耐油、High Dimensional Stability
材料用途：机器/机械部件、汽车领域的应用、容器、外壳
加工方法：黑色粒子注射成型
供货地区：北美洲
中国代理：苏州希普能工程塑料
Ultramid® A3WG6 BK00564 加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.36 | g/cm³ | ISO 1183 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 5.5 | % | |
| 平衡,23℃,50% RH | 1.7 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸应力(断裂,23℃) | 179 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 2.6 | % | ISO 527-2 |
| 弯曲模量(23℃) | 8730 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 悬壁梁缺口冲击强度(23℃) | 8.5 | kJ/m² | ISO 180 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 250 | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 260 | ℃ | ISO 3146 |
| RTI Elec | UL 746B | ||
| 0.71 mm | 125 | ℃ | |
| 1.5 mm | 125 | ℃ | |
| 3.0 mm | 125 | ℃ | |
| RTI Imp | UL 746B | ||
| 1.5 mm | 115 | ℃ | |
| 3.0 mm | 120 | ℃ | |
| RTI | UL 746B | ||
| 1.5 mm | 115 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.71 mm | HB | ||
| 1.5 mm | HB | ||
| 3.0 mm | HB | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 280 到 305 | ℃ | |
| 模具温度 | 80 到 90 | ℃ | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||