Ultramid® 8232G HS FR BK102
聚酰胺6
BASF Corporation
Product Description:
Ultramid 8232G HS FR BK102 is a 25% glass fiber reinforced, heat stabilized, flame retardant pigmented black PA6 injection molding compound exhibiting excellent melt stability characteristics. It combines flame retardant ability with an excellent balance of high strength, stiffness and heat distortion temperature.
Applications
Ultramid 8232G HS FR BK102 is generally recommended for applications such as connectors, terminal blocks, switches and receptacles, coil bobbins, and appliance housings.
黄卡号码：E36632-231124
填料增强：玻璃纤维增强材料,25%填料按重量
有添加剂：热稳定剂
粒料特性：高刚性、高强度、较高的熔体稳定性、热稳定、阻燃
粒料用途：家电部件、开关、连接器、外壳、线轴
外观颜色：黑色粒子
加工方法：注射成型
供货地区：北美洲
物料参数
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 / 比重 | 1.67 | g/cm³ | ASTM D792,ISO 1183 |
| 收缩率 - 流动(3.18 mm) | 0.30 | % | |
| 吸水率 | |||
| 饱和 | 4.0 | % | ASTM D570 |
| 饱和,23℃ | 4.0 | % | ISO 62 |
| 平衡,50% RH | 1.1 | % | ASTM D570 |
| 平衡,23℃,50% RH | 1.1 | % | ISO 62 |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 级) | 121 | ASTM D785 | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 11000 | MPa | ISO 527-2 |
| 抗张强度(断裂,23℃) | 150 | MPa | ASTM D638,ISO 527-2 |
| 伸长率(断裂,23℃) | 1.9 | % | ASTM D638,ISO 527-2 |
| 弯曲模量(23℃) | 10400 | MPa | ASTM D790,ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30℃ | 8.0 | kJ/m² | |
| 23℃ | 9.4 | kJ/m² | |
| 简支梁无缺口冲击强度(23℃) | 50 | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 | |||
| 23℃ | 77 | J/m | ASTM D256 |
| 23℃ | 9.8 | kJ/m² | ISO 180 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 1.8 MPa,未退火 | 205 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 195 | ℃ | ISO 75-2/A |
| 熔融峰值温度 | 220 | ℃ | ASTM D3418,ISO 3146 |
| RTI Elec | UL 746 | ||
| 0.75 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 2.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI Imp | UL 746 | ||
| 0.75 mm | 105 | ℃ | |
| 1.5 mm | 115 | ℃ | |
| 2.5 mm | 115 | ℃ | |
| 3.0 mm | 115 | ℃ | |
| RTI | UL 746 | ||
| 0.75 mm | 105 | ℃ | |
| 1.5 mm | 115 | ℃ | |
| 2.5 mm | 115 | ℃ | |
| 3.0 mm | 120 | ℃ | |
| 可燃性 | 额定值 | 测试方法 | |
| UL 阻燃等级 | UL 94 | ||
| 0.75 mm | V-0 | ||
| 1.5 mm | V-0 | ||
| 2.5 mm | V-0 | ||
| 5VA | |||
| 3.0 mm | V-0 | ||
| 5VA | |||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.15 | % | |
| 加工（熔体）温度 | 250 到 290 | ℃ | |
| 模具温度 | 80 到 95 | ℃ | |
| 注塑压力 | 3.50 到 12.5 | MPa | |
| 注射速度 | 快速 | ||