NORYL™ LPN170HG
聚苯醚 + PS (PPE+PS)
SABIC 沙特基础工业公司
NORYL LPN170HG resin is a non-reinforced blend of polyphenylene ether (PPE) + polystyrene (PS) designed for high heat resistance, low density, high gloss, low outgassing and good dimensional stability performance. This extrusion and injection moldable grade carries HDT 170℃, special gravity 1.07 g/cm3. This grade is capable for physical vapor deposition with good light distribution and high reflection rate. LPN170HG is targeted for automotive headlamp reflector, bezel, trim, light shielding and other high surface quality / high heat resistance demanded components.
材料特性：尺寸稳定性良好，高耐热，水解稳定，PFAS not intentionally added
材料用途：电器用具，反射镜，汽车领域的应用，汽车外部零件，汽车照明，照明应用，LEDs
外观加工：挤出，注射成型粒子
供货地区：北美洲，非洲和中东，拉丁美洲，欧洲，亚太地区
沙伯代理：苏州希普能工程塑料
NORYL™ LPN170HG SABIC中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.07 | g/cm³ | ASTM D792 |
| 熔流率（熔体流动速率）(300℃/5.0 kg) | 8.7 | g/10 min | ASTM D1238 |
| 收缩率 | 内部方法 | ||
| 垂直:3.20 mm | 0.84 | % | |
| 流动:3.20 mm | 0.83 | % | |
| 吸水率(24 hr,23℃) | 0.023 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 2630 | MPa | ASTM D638 |
| -- | 2640 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服2 | 78.0 | MPa | ASTM D638 |
| 屈服 | 78.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服2 | 5.2 | % | ASTM D638 |
| 屈服 | 5.3 | % | ISO 527-2/5 |
| 断裂2 | 31 | % | ASTM D638 |
| 断裂 | 15 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 2660 | MPa | ASTM D790 |
| --4 | 2780 | MPa | ISO 178 |
| 弯曲强度 | |||
| 50.0 mm 跨距3 | 124 | MPa | ASTM D790 |
| --4 | 125 | MPa | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 悬壁梁缺口冲击强度 | |||
| -40℃ | 35 | J/m | ASTM D256 |
| 23℃ | 30 | J/m | ASTM D256 |
| -40℃5 | 4.3 | kJ/m² | ISO 180/1A |
| 23℃5 | 4.3 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -40℃ | 700 | J/m | ASTM D4812 |
| 23℃ | 790 | J/m | ASTM D4812 |
| -40℃5 | 43 | kJ/m² | ISO 180/1U |
| 23℃5 | 72 | kJ/m² | ISO 180/1U |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,6.40 mm | 180 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm跨距5 | 177 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,6.40 mm | 170 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm跨距5 | 163 | ℃ | ISO 75-2/Af |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动:-40 到 40℃ | 5.8E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 5.9E-5 | cm/cm/℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | 9.2E+16 | ohms | ASTM D257 |
| 体积电阻率 | 9.2E+16 | ohms·cm | ASTM D257 |
| 光学性能 | 额定值 | 单位制 | 测试方法 |
| 光泽度 | ASTM D2457 | ||
| 45° | 101 | ||
| 60° | 102 | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 100 到 120 | ℃ | |
| 干燥时间 | 3.0 到 5.0 | hr | |
| 料筒后部温度 | 280 到 340 | ℃ | |
| 料筒中部温度 | 280 到 340 | ℃ | |
| 料筒前部温度 | 300 到 340 | ℃ | |
| 射嘴温度 | 300 到 340 | ℃ | |
| 加工（熔体）温度 | 300 到 340 | ℃ | |
| 模具温度 | 80 到 150 | ℃ | |
| 背压 | 2.00 到 10.0 | MPa | |
| 螺杆转速 | 20 到 100 | rpm | |
| 备注 15.0 mm/min 2类型 1,5.0 mm/min 31.3 mm/min 42.0 mm/min 580*10*4 mm |
|||