NORYL GTX™ GTX678
聚苯醚+PS+尼龙
SABIC
产品说明:
NORYL GTX678 resin is a conductive, high performance non-reinforced alloy of Polyphenylene Ether (PPE) + Polyamide (PA). This injection moldable grade is optimized for primer-less electrostatic and powder coat painting, and it is UL 5VA rated with a non-brominated, non-chlorinated FR package. NORYL GTX678 resin exhibits an excellent balance of conductivity, high heat resistance, good ductility, and is heat stabilized. This material is an excellent candidate for non-automotive painted applications such as office furniture, PVC/metal replacement, lighting ballast housings / enclosures, and appliance exteriors.
含添加剂：冲击改性剂、热稳定剂、阻燃
材料特性：Low Specific Gravity、尺寸稳定性良好、冲击改性、导电、低翘曲、低吸湿、高刚性、高强度、良好抗撞击性、耐化学品、耐热高、热稳定、收缩性低、水解稳定、外观良好、无卤阻燃
材料用途：安全帽、电脑组件、电气/电子应用领域、电器用具、建筑材料、手机、照明应用
加工方法：注射成型
供货地区：亚太地区
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.12 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(300℃/5.0 kg) | 7.8 | g/10 min | ASTM D1238 |
| 熔融体积流量（MVR）(300℃/5.0 kg) | 7.0 | cm³/10min | ISO 1133 |
| 收缩率-流动(3.20 mm) | 1.3 到 1.5 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 4.0 | % | |
| 平衡,23℃,50% RH | 0.50 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 2900 | MPa | ASTM D638 |
| -- | 2900 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服2 | 58.0 | MPa | ASTM D638 |
| 屈服 | 58.0 | MPa | ISO 527-2/50 |
| 断裂2 | 52.0 | MPa | ASTM D638 |
| 断裂 | 52.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服2 | 7.0 | % | ASTM D638 |
| 屈服 | 7.0 | % | ISO 527-2/50 |
| 断裂2 | 12 | % | ASTM D638 |
| 断裂 | 12 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 2600 | MPa | ASTM D790 |
| --4 | 2600 | MPa | ISO 178 |
| 弯曲应力 | |||
| --4,5 | 95.0 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 95.0 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度6(23℃) | 12 | kJ/m² | ISO 179/1eA |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 70 | J/m | ASTM D256 |
| 23℃ | 100 | J/m | ASTM D256 |
| -30℃7 | 7.0 | kJ/m² | ISO 180/1A |
| 23℃7 | 10 | kJ/m² | ISO 180/1A |
| 装有测量仪表的落镖冲击(23℃,Total Energy) | 60.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 195 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm 跨距7 | 191 | ℃ | ISO 75-2/Bf |
| 维卡软化温度 | |||
| -- | 198 | ℃ | ASTM D15258 |
| -- | 195 | ℃ | ISO 306/B120 |
| -- | 197 | ℃ | ISO 306/B50 |
| Ball Pressure Test(123 到 127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动:-40 到 40℃ | 7.8E-5 | cm/cm/℃ | ASTM E831 |
| 流动:23 到 60℃ | 8.3E-5 | cm/cm/℃ | ISO 11359-2 |
| 垂直:-40 到 40℃ | 8.0E-5 | cm/cm/℃ | ASTM E831 |
| 垂直:23 到 60℃ | 8.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 比热 | 1400 | J/kg/℃ | ASTM C351 |
| 导热系数 | 0.20 | W/m/K | ASTM C177 |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 体积电阻率 | 4000 | ohms·cm | ASTM D257 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 95 到 105 | ℃ | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.070 | % | |
| 建议注射量 | 30 到 50 | % | |
| 料筒后部温度 | 260 到 300 | ℃ | |
| 料筒中部温度 | 265 到 300 | ℃ | |
| 料筒前部温度 | 270 到 300 | ℃ | |
| 射嘴温度 | 275 到 300 | ℃ | |
| 加工（熔体）温度 | 275 到 300 | ℃ | |
| 模具温度 | 65 到 95 | ℃ | |
| 背压 | 0.300 到 1.40 | MPa | |
| 螺杆转速 | 20 到 100 | rpm | |
| 排气孔深度 | 0.013 到 0.038 | mm | |
| 注射说明 Drying Time (Cumulative): 8 hr Minimum Moisture Content: 0.02% 挤压说明 Profile Extrusion Parameters Drying Temperature: 105 to 110℃ Drying Time: 8 hr Drying Time (Cumulative): 24 hr Maximum Moisture Content: 0.03% Barrel-Zone 1 Temperature: 245 to 260℃ Barrel-Zone 2 Temperature: 245 to 260℃ Barrel-Zone 3 Temperature: 245 to 260℃ Barrel-Zone 4 Temperature: 245 to 260℃ Adapter Temperature: 245 to 260℃ Die Temperature: 245 to 260℃ Melt Temperature: 245 to 260℃ Calibrator Temperature: 35 to 75℃ Water Bath Temperature: 40-50℃ 备注 15.0 mm/min 2类型 1,50 mm/min 31.3 mm/min 42.0 mm/min 5at Yield 680*10*4 sp=62mm 780*10*4 mm 8速率 A (50℃/h),载荷2 (50N) |
|||
NORYL™树脂系列是建立在SABIC的基础上的专有的聚苯醚(PPE)技术。
NORYL树脂在注塑成型方面表现出广泛的应用前景一系列杰出的特性应用于：水管理，汽车，电气，太阳能，能源储存，建筑和建筑，电器还有许多其他行业。
NORYL树脂，它是由高抗冲击聚苯乙烯(HIPS)，呈无定形特征。
NORYL GTX和NORYL PPX树脂利用流动特性和耐化学性半结晶材料，同时添加好尺寸稳定，吸湿性低
非晶态PPE具有低蠕变倾向技术。
noryl™系列树脂
NORYL系列树脂代表了SABIC创新的聚苯醚(PPE)的组合。高冲击聚苯乙烯(HIPS)，聚丙烯(PP)，聚酰胺(PA)混合技术或热塑性弹性体(TPE)，连同选定的添加剂和填料。
通过将两种树脂的强度按顺序结合在一起，创造了这些混合物，从而增加了价值满足关键要求，如耐化学性、模数和可加工性。
作为NORYL树脂家族的基石，PPE提供了独特的组合增强其通用性的属性。
PPE的特点包括:
•非常低的水分吸收
•优异的水解稳定性/抗水解性
•长期尺寸稳定性-即使在高温，水，潮湿的环境
•在各种环境下保持机械性能;包括紫外线(UV)曝光
•非常低的比重
•低翘曲+低蠕变
•优异的电绝缘性能，由于高介电强度
•良好的冲击、拉伸强度和弯曲强度
•阻燃等级均为非溴化和非氯化
•高耐热性允许具有成本效益，高温性能
应用程序开发注意事项
NORYL™树脂一直被认为是最终用途应用的材料选择，例如水管理、医疗保健和汽车内饰等行业接触化学物质和清洁剂是很常见的。这是最重要的应用程序开发和材料选择的考虑因素是环境中的最终产品将被使用。这不仅包括暴露于温度极端，还会受到天气、紫外线、过度潮湿、溶剂等的影响化学物质。
接触化学物质的影响
在许多行业中，最终用途应用程序都有可能暴露对无数的化学品和/或清洁剂。这种接触可能导致:
•物理降解-应力开裂，开裂，软化，肿胀，变色
•性能下降-化学品与聚合物的反应可能导致热塑性塑料的机械性能或其它性能的丧失