Ultramid® 8253 HS
聚酰胺6
BASF Corporation
Product Description:
This resin is a heat stabilized, impact modified type 6 graft copolymer developed for both injection molding and extrusion applications requiring improved dry as molded toughness and increased flexibility. It is also available in non-heat stabilized (Ultramid 8253) and/or pigmented versions.
Applications
Ultramid 8253 HS is generally recommended for applications such as plugs, receptacles, flexible connector covers, weed trimmer components, clips, fasteners, flanges, key housings as well as many flexible tubing applications.
黄卡号码：E36632-231135
有添加剂：热稳定剂、冲击改性剂
粒料特性：冲击改性、共聚物、良好的柔韧性、热稳定性、韧性良好
粒料用途：保护性遮盖物、草坪和园林设备、插头、管件、紧固件、外壳
外观颜色：可用颜色、BK102
加工方法：挤出、注射成型
供货地区：亚太地区、北美洲
物料参数
| 物理性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 密度 / 比重 | 1.09 | -- | g/cm³ | ASTM D792,ISO 1183 |
| 收缩率 - 流动(3.18 mm) | 1.2 | -- | % | |
| 吸水率 | ||||
| 24 hr | 1.5 | -- | % | ASTM D570 |
| 24 hr,23℃ | 1.5 | -- | % | ISO 62 |
| 饱和 | 8.1 | -- | % | ASTM D570 |
| 饱和,23℃ | 8.1 | -- | % | ISO 62 |
| 平衡,50% RH | 2.3 | -- | % | ASTM D570 |
| 平衡,23℃,50% RH | 2.3 | -- | % | ISO 62 |
| 硬度 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 洛氏硬度(R 级) | 82 | -- | ASTM D785 | |
| 机械性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 拉伸模量 | ISO 527-2 | |||
| -40℃ | 2840 | 3300 | MPa | |
| 23℃ | 2300 | 730 | MPa | |
| 80℃ | 400 | 370 | MPa | |
| 120℃ | 295 | 220 | MPa | |
| 150℃ | 250 | 220 | MPa | |
| 抗张强度 | ||||
| 屈服,-40℃ | 117 | 116 | MPa | ASTM D638,ISO 527-2 |
| 屈服,23℃ | 65.0 | 32.0 | MPa | ASTM D638 |
| 屈服,80℃ | 25.0 | 20.0 | MPa | ASTM D638,ISO 527-2 |
| 屈服,121℃ | 20.0 | -- | MPa | ASTM D638 |
| 屈服,23℃ | 60.0 | 32.0 | MPa | ISO 527-2 |
| 屈服,120℃ | 20.0 | -- | MPa | ISO 527-2 |
| 屈服,150℃ | 15.0 | 15.0 | MPa | ISO 527-2 |
| 断裂,-40℃ | 100 | 70.0 | MPa | ASTM D638 |
| 断裂,23℃ | 60.0 | -- | MPa | ASTM D638 |
| 伸长率 | ||||
| 屈服,-40℃ | 7.0 | -- | % | ASTM D638 |
| 屈服,23℃ | 4.0 | 15 | % | ASTM D638,ISO 527-2 |
| 屈服,80℃ | 29 | -- | % | ASTM D638 |
| 屈服,121℃ | 34 | 30 | % | ASTM D638 |
| 断裂,-40℃ | 9.0 | 20 | % | ASTM D638 |
| 断裂,23℃ | > 100 | > 100 | % | ASTM D638 |
| 标称拉伸断裂应变 | ISO 527-2 | |||
| -40℃ | 9.0 | 20 | % | |
| 23℃ | 40 | > 50 | % | |
| 弯曲模量 | ||||
| -40℃ | 3050 | 3150 | MPa | ASTM D790 |
| 23℃ | 2210 | 670 | MPa | ASTM D790 |
| 65℃ | 415 | -- | MPa | ASTM D790 |
| 90℃ | 325 | -- | MPa | ASTM D790 |
| 121℃ | 260 | -- | MPa | ASTM D790 |
| 23℃ | 1900 | -- | MPa | ISO 178 |
| 弯曲强度 | ||||
| -40℃ | 148 | 141 | MPa | ASTM D790 |
| 23℃ | 87.0 | 32.0 | MPa | ASTM D790 |
| 65℃ | 25.0 | -- | MPa | ASTM D790 |
| 90℃ | 20.0 | -- | MPa | ASTM D790 |
| 121℃ | 14.0 | -- | MPa | ASTM D790 |
| 23℃ | 65.0 | -- | MPa | ISO 178 |
| 冲击性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | |||
| -30℃ | 5.0 | -- | kJ/m² | |
| 23℃ | 18 | -- | kJ/m² | |
| 简支梁无缺口冲击强度(23℃) | 无断裂 | -- | ISO 179 | |
| 悬壁梁缺口冲击强度 | ASTM D256 | |||
| -40℃ | 80 | 64 | J/m | |
| 23℃ | 150J/m | 无断裂 | ||
| Drop Impact Resistance(23℃) | 271 | > 271 | J | 内部方法 |
| 热性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 载荷下热变形温度 | ||||
| 0.45 MPa,未退火 | 168 | -- | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 160 | -- | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 60.0 | -- | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 55.0 | -- | ℃ | ISO 75-2/A |
| 熔融峰值温度 | 220 | -- | ℃ | ASTM D3418,ISO 3146 |
| 线形热膨胀系数 | ||||
| 流动 | 9.9E-5 | -- | cm/cm/℃ | ASTM E831 |
| 流动 | 8.8E-5 | -- | cm/cm/℃ | |
| 垂直 | 9.3E-5 | -- | cm/cm/℃ | |
| RTI Elec | UL 746 | |||
| 0.71 mm | 105 | -- | ℃ | |
| 0.75 mm | 105 | -- | ℃ | |
| 1.5 mm | 105 | -- | ℃ | |
| 3.0 mm | 105 | -- | ℃ | |
| 6.0 mm | 105 | -- | ℃ | |
| RTI Imp | UL 746 | |||
| 0.71 mm | 95.0 | -- | ℃ | |
| 0.75 mm | 95.0 | -- | ℃ | |
| 1.5 mm | 105 | -- | ℃ | |
| 3.0 mm | 105 | -- | ℃ | |
| 6.0 mm | 105 | -- | ℃ | |
| RTI | UL 746 | |||
| 0.71 mm | 95.0 | -- | ℃ | |
| 0.75 mm | 95.0 | -- | ℃ | |
| 1.5 mm | 105 | -- | ℃ | |
| 3.0 mm | 105 | -- | ℃ | |
| 6.0 mm | 105 | -- | ℃ | |
| 电气性能 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| 体积电阻率 | ||||
| 1.50 mm | > 1.0E+15 | -- | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | -- | ohms·cm | IEC 60093 |
| 漏电起痕指数 | 600 | -- | V | IEC 60112 |
| 可燃性 | 干燥 | 调节后的 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | |||
| 0.75 mm | HB | -- | ||
| 1.5 mm | HB | -- | ||
| 3.0 mm | HB | -- | ||
| 6.0 mm | HB | -- | ||
| 注射 | 干燥 | 单位制 | ||
| 干燥温度 | 80 | ℃ | ||
| 干燥时间 | 2.0 到 4.0 | hr | ||
| 建议的最大水分含量 | 0.20 | % | ||
| 加工（熔体）温度 | 240 到 270 | ℃ | ||
| 模具温度 | 60 到 85 | ℃ | ||
| 注塑压力 | 3.50 到 12.5 | MPa | ||
| 注射速度 | 快速 | |||