Ultradur® B 4406
聚丁烯对苯二甲酸酯(PBT)
德国巴斯夫-BASF Corporation
产品说明:
Ultradur B 4406 is an injection molding PBT grade grade with migration-free flame retardant offering a UL V0 rating.
Applications
Typical applications include relay housings, plug-in connectors, and switch and lamp parts.
ul证书号：E41871-233793
含添加剂：阻燃剂
材料特性：无迁移阻燃
材料用途：开关，连接器，外壳
加工方法：粒子注射成型
供货地区：北美洲，亚太地区，欧洲
中国代理：苏州希普能工程塑料
Ultradur® B 4406巴斯夫中文加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.45 | g/cm³ | ASTM D792,ISO 1183 |
| 熔融体积流量（MVR）(250℃/2.16kg) | 30 | cm³/10min | ISO 1133 |
| 收缩率-流动(3.18 mm) | 1.5 | % | |
| 吸水率 | |||
| 饱和 | 0.40 | % | ASTM D570 |
| 饱和,23℃ | 0.40 | % | ISO 62 |
| 平衡,50% RH | 0.25 | % | ASTM D570 |
| 平衡,23℃,50% RH | 0.25 | % | ISO 62 |
| Viscosity Number (Reduced Viscosity) | 122.0 | ml/g | ISO 1628 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 3000 | MPa | ISO 527-1 |
| 抗张强度(屈服,23℃) | 65.0 | MPa | ASTM D638,ISO 527-2 |
| 伸长率(屈服,23℃) | 3.9 | % | ASTM D638,ISO 527-2 |
| 标称拉伸断裂应变 | ISO 527-2 | ||
| -40℃ | 3.3 | % | |
| 23℃ | 3.5 | % | |
| 拉伸蠕变模量(1hr) | 1800 | MPa | ISO 899-1 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30℃ | 4.0 | kJ/m² | |
| 23℃ | 4.0 | kJ/m² | |
| 简支梁无缺口冲击强度(23℃) | 50 | kJ/m² | ISO 179 |
| 悬壁梁缺口冲击强度 | ASTM D256 | ||
| -40℃ | 37 | J/m | |
| 23℃ | 37 | J/m | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火 | 165 | ℃ | ASTM D648 |
| 0.45 MPa,未退火 | 170 | ℃ | ISO 75-2/B |
| 1.8 MPa,未退火 | 80.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火 | 60.0 | ℃ | ISO 75-2/A |
| 熔融峰值温度 | 223 | ℃ | ASTM D3418,ISO 3146 |
| 线形热膨胀系数-流动 | |||
| -- | 9.0E-5 | cm/cm/℃ | ASTM E831 |
| -- | 5.5E-5 | cm/cm/℃ | |
| RTI Elec | UL 746B | ||
| 0.75 mm | 125 | ℃ | |
| 1.5 mm | 125 | ℃ | |
| 3.0 mm | 125 | ℃ | |
| RTI Imp | UL 746B | ||
| 0.75 mm | 130 | ℃ | |
| 1.5 mm | 130 | ℃ | |
| 3.0 mm | 130 | ℃ | |
| RTI | UL 746B | ||
| 0.75 mm | 140 | ℃ | |
| 1.5 mm | 140 | ℃ | |
| 3.0 mm | 140 | ℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | |||
| 1.50 mm | 1.0E+13 | ohms | ASTM D257 |
| -- | 1.0E+13 | ohms | IEC 60093 |
| 体积电阻率 | |||
| 1.50 mm | > 1.0E+15 | ohms·cm | ASTM D257 |
| -- | > 1.0E+15 | ohms·cm | IEC 60093 |
| 介电常数 | IEC 60250 | ||
| 100 Hz | 3.30 | ||
| 1 MHz | 3.30 | ||
| 耗散因数 | IEC 60250 | ||
| 100 Hz | 0.011 | ||
| 1 MHz | 0.017 | ||
| 漏电起痕指数 | 250 | V | IEC 60112 |
| 可燃性 | 额定值 | 单位制 | 测试方法 |
| UL 阻燃等级 | UL 94 | ||
| 0.40 mm | V-0 | ||
| 0.75 mm | V-0 | ||
| 1.5 mm | V-0 | ||
| 3.0 mm | V-0 | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 100到120 | ℃ | |
| 干燥时间 | 4.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 加工（熔体）温度 | 250到270 | ℃ | |
| 模具温度 | 40到80 | ℃ | |
| 注塑压力 | 3.50到12.5 | MPa | |
| 注射速度 | 快速 | ||
| 背压 | < 1.00 | MPa | |