CYCOLOY™ FR Resin CX7110 - Asia
聚碳酸酯+丙烯腈丁二烯苯乙烯
SABIC
产品说明:
CYCOLOY CX7110 Polycarbonate/Acrylonitrile Butadiene Styrene (PC/ABS) blend is an injection moldable, high flow, non chlorinated/brominated flame retardant grade. It has a UL94 V0@1.8mm and 5VB@1.2mm flame rating. This grade has improved chemical resistance compared to standard PC/ABS blends and is a good candidate for thin wall applications.
供货地区：亚太地区
黄卡认证：E207780-566196
粒料用途：电气/电子应用领域、电器用具、电子显示器
物料参数
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.19 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(260℃/2.16 kg) | 22 | g/10 min | ASTM D1238 |
| 熔融体积流量（MVR）(260℃/2.16 kg) | 21 | cm³/10min | ISO 1133 |
| 收缩率 - 流动(3.20 mm) | 0.40 到 0.60 | % | 内部方法 |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.20 | % | |
| 平衡,23℃,50% RH | 0.10 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --1 | 2900 | MPa | ASTM D638 |
| -- | 2700 | MPa | ISO 527-2/1 |
| 抗张强度 | |||
| 屈服2 | 64.0 | MPa | ASTM D638 |
| 屈服 | 61.0 | MPa | ISO 527-2/50 |
| 断裂2 | 54.0 | MPa | ASTM D638 |
| 断裂 | 51.0 | MPa | ISO 527-2/50 |
| 伸长率 | |||
| 屈服2 | 4.0 | % | ASTM D638 |
| 屈服 | 4.0 | % | ISO 527-2/50 |
| 断裂2 | 90 | % | ASTM D638 |
| 断裂 | 90 | % | ISO 527-2/50 |
| 弯曲模量 | |||
| 50.0 mm 跨距3 | 2700 | MPa | ASTM D790 |
| --4 | 2500 | MPa | ISO 178 |
| 弯曲应力 | |||
| --4,5 | 100 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距3 | 100 | MPa | ASTM D790 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度6 | ISO 179/1eA | ||
| -30℃ | 10 | kJ/m² | |
| 23℃ | 15 | kJ/m² | |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 120 | J/m | ASTM D256 |
| 23℃ | 600 | J/m | ASTM D256 |
| -30℃7 | 10 | kJ/m² | ISO 180/1A |
| 23℃7 | 15 | kJ/m² | ISO 180/1A |
| 装有测量仪表的落镖冲击(23℃,Total Energy) | 63.0 | J | ASTM D3763 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 94.0 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,6.40 mm | 98.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,3.20 mm | 84.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,6.40 mm | 90.0 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm 跨距8 | 84.0 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 102 | ℃ | ASTM D15259,ISO 306/B509 |
| -- | 103 | ℃ | ISO 306/B120 |
| Ball Pressure Test(73 到 77℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | |||
| 流动 : -40 到 40℃ | 7.5E-5 | cm/cm/℃ | ASTM E831,ISO 11359-2 |
| 垂直 : -40 到 40℃ | 7.5E-5 | cm/cm/℃ | ASTM E831 |
| 垂直 : -40℃ | 7.5E-5 | cm/cm/℃ | ISO 11359-2 |
| 导热系数 | 0.20 | W/m/K | ISO 8302 |
| RTI Elec10 | 90.0 | ℃ | UL 746 |
| RTI Imp10 | 90.0 | ℃ | UL 746 |
| RTI10 | 90.0 | ℃ | UL 746 |
| 可燃性 | 额定值 | 测试方法 | |
| UL 阻燃等级 | UL 94 | ||
| > 0.75 mm | V-2 | ||
| > 1.0 mm | V-1 | ||
| > 1.2 mm | V-0 | ||
| > 1.8 mm | 5VB | ||
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 80 到 90 | ℃ | |
| 干燥时间 | 3.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.040 | % | |
| 建议注射量 | 30 到 80 | % | |
| 料筒后部温度 | 220 到 255 | ℃ | |
| 料筒中部温度 | 220 到 265 | ℃ | |
| 料筒前部温度 | 245 到 275 | ℃ | |
| 射嘴温度 | 245 到 275 | ℃ | |
| 加工（熔体）温度 | 245 到 275 | ℃ | |
| 模具温度 | 60 到 80 | ℃ | |
| 背压 | 0.300 到 0.700 | MPa | |
| 螺杆转速 | 40 到 70 | rpm | |
| 排气孔深度 | 0.038 到 0.076 | mm | |
| 注射说明 Injection Molding Parameters *Drying Time (Cumulative): 8 hrs 备注 150 mm/min 2类型 1,50 mm/min 31.3 mm/min 42.0 mm/min 5at Yield 680*10*3 sp=62mm 780*10*3 mm 880*10*4 mm 9速率 A (50℃/h),载荷2 (50N) 10UL Ratings shown on the technical datasheet might not cover the full range of thicknesses and colors. For details,please see the UL Yellow Card. |
|||
“Cycoloy”由聚碳酸酯（Polycarbonate）和聚丙烯精（ABS）合金而成的热可塑性塑胶，“Cycoloy”结合了两种材料的优异特性，ABS材料的成型性和PC的机械性、抗冲击性、流动性、抗紫外线（UV）和耐高温等性质，可广泛使用在汽车内部零件、事务机器、通信器材、家电用品及照明设备上等电器元件。