SABIC VALOX™ VX4915R
聚对苯二甲酸丁二酯 + ASA (PBT+ASA)
15% Glass reinforced nucleated PBT/ASA improved release, with excellent mechanical properties high dimensional stability, and low density.
材料用途：电气/电子应用领域
供货地区：欧洲
物料性能：
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度/比重 | 1.31 | g/cm³ | ASTM D792,ISO 1183 |
| 熔流率（熔体流动速率）(265℃/5.0 kg) | 33 | g/10 min | ASTM D1238 |
| 熔融体积流量（MVR） | ISO 1133 | ||
| 250℃/5.0 kg | 20 | cm³/10min | |
| 265℃/5.0 kg | 30 | cm³/10min | |
| 收缩率2 | 内部方法 | ||
| 垂直 | 0.30 到 0.70 | % | |
| 流动 | 0.20 到 0.60 | % | |
| 吸水率 | ISO 62 | ||
| 饱和,23℃ | 0.80 | % | |
| 平衡,23℃,50% RH | 0.30 | % | |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量 | |||
| --3 | 5600 | MPa | ASTM D638 |
| -- | 5700 | MPa | ISO 527-1/1 |
| 抗张强度 | |||
| 屈服4 | 85.0 | MPa | ASTM D638 |
| 屈服 | 80.0 | MPa | ISO 527-2/5 |
| 断裂4 | 85.0 | MPa | ASTM D638 |
| 断裂 | 80.0 | MPa | ISO 527-2/5 |
| 伸长率 | |||
| 屈服4 | 3.0 | % | ASTM D638 |
| 屈服 | 4.0 | % | ISO 527-2/5 |
| 断裂4 | 3.0 | % | ASTM D638 |
| 断裂 | 4.0 | % | ISO 527-2/5 |
| 弯曲模量 | |||
| 50.0 mm 跨距5 | 4200 | MPa | ASTM D790 |
| --6 | 4600 | MPa | ISO 178 |
| 弯曲应力 | |||
| --6,7 | 130 | MPa | ISO 178 |
| 屈服,50.0 mm 跨距5 | 125 | MPa | ASTM D790 |
| 断裂,50.0 mm 跨距5 | 125 | MPa | ASTM D790 |
| 弯曲应变-at Break8 | 4.0 | % | ISO 178 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179/2C | ||
| -30℃ | 6.0 | kJ/m² | |
| 23℃ | 6.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179/2U | ||
| -30℃ | 30 | kJ/m² | |
| 23℃ | 45 | kJ/m² | |
| 悬壁梁缺口冲击强度 | |||
| -30℃ | 50 | J/m | ASTM D256 |
| 0℃ | 60 | J/m | ASTM D256 |
| 23℃ | 65 | J/m | ASTM D256 |
| -30℃9 | 5.0 | kJ/m² | ISO 180/1A |
| 0℃9 | 6.0 | kJ/m² | ISO 180/1A |
| 23℃9 | 6.0 | kJ/m² | ISO 180/1A |
| 无缺口悬臂梁冲击 | |||
| -30℃ | 490 | J/m | ASTM D4812 |
| 23℃ | 520 | J/m | ASTM D4812 |
| -30℃9 | 25 | kJ/m² | ISO 180/1U |
| 23℃9 | 35 | kJ/m² | ISO 180/1U |
| 硬度 | 额定值 | 单位制 | 测试方法 |
| 洛氏硬度(R 计秤) | 120 | ISO 2039-2 | |
| 球压硬度(H 358/30) | 100 | MPa | ISO 2039-1 |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度 | |||
| 0.45 MPa,未退火,3.20 mm | 200 | ℃ | ASTM D648 |
| 0.45 MPa,未退火,4.00 mm,64.0 mm跨距9 | 200 | ℃ | ISO 75-2/Bf |
| 1.8 MPa,未退火,3.20 mm | 105 | ℃ | ASTM D648 |
| 1.8 MPa,未退火,4.00 mm,64.0 mm跨距9 | 105 | ℃ | ISO 75-2/Af |
| 维卡软化温度 | |||
| -- | 213 | ℃ | ASTM D152510,ISO 306/A5010 |
| -- | 135 | ℃ | ASTM D152511,ISO 306/B120,ISO 306/B50 |
| Ball Pressure Test(123 到127℃) | 通过 | IEC 60695-10-2 | |
| 线形热膨胀系数 | ISO 11359-2 | ||
| 流动:-40 到 40℃ | 8.3E-5 | cm/cm/℃ | |
| 流动:23 到 60℃ | 4.0E-5 | cm/cm/℃ | |
| 流动:23 到 150℃ | 2.7E-5 | cm/cm/℃ | |
| 垂直:-40 到 40℃ | 8.2E-5 | cm/cm/℃ | |
| 垂直:23 到 60℃ | 1.0E-4 | cm/cm/℃ | |
| 垂直:23 到 150℃ | 1.9E-4 | cm/cm/℃ | |
| 电气性能 | 额定值 | 单位制 | 测试方法 |
| 表面电阻率 | > 1.0E+15 | ohms | IEC 60093 |
| 体积电阻率 | > 1.0E+15 | ohms·cm | ASTM D257,IEC 60093 |
| 介电强度 | |||
| 1.60 mm,in Oil | 22 | kV/mm | ASTM D149 |
| 3.20 mm,in Oil | 17 | kV/mm | ASTM D149 |
| 1.60 mm,在油中 | 22 | kV/mm | IEC 60243-1 |
| 3.20 mm,在油中 | 17 | kV/mm | IEC 60243-1 |
| 介电常数(1 MHz) | 3.00 | ASTM D150,IEC 60250 | |
| 耗散因数(1 MHz) | 0.020 | ASTM D150,IEC 60250 | |
| 漏电起痕指数 | 575 | V | IEC 60112 |
| 充模分析 | 额定值 | 单位制 | 测试方法 |
| 熔体粘度(260℃,1500 sec^-1) | 155 | Pa·s | ISO 11443 |
| 补充信息 | 额定值 | 单位制 | 测试方法 |
| 填充物 | 15 | % | ASTM D229 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 | 110 到 120 | ℃ | |
| 干燥时间 | 2.0 到 4.0 | hr | |
| 建议的最大水分含量 | 0.020 | % | |
| 料斗温度 | 40 到 60 | ℃ | |
| 料筒后部温度 | 230 到 245 | ℃ | |
| 料筒中部温度 | 240 到 255 | ℃ | |
| 料筒前部温度 | 245 到 265 | ℃ | |
| 射嘴温度 | 240 到 260 | ℃ | |
| 加工（熔体）温度 | 250 到 270 | ℃ | |
| 模具温度 | 40 到 100 | ℃ | |
| 备注 1一般属性：这些不能被视为规格。 2Tensile Bar 35.0 mm/min 4类型 1, 5.0 mm/min 51.3 mm/min 62.0 mm/min 7at Yield 82 mm/min 980*10*4 mm 10速率 A (50℃/h), 压 力1 (10N) 11速率 A (50℃/h), 载荷2 (50N) |
|||