Ultramid® Advanced N3HG6
聚酰胺 9T （尼龙 9T）PA9T
德国巴斯夫-BASF Corporation
产品说明:
Preliminary Product - Ultramid Advanced N3HG6 is a partially aromatic, 30% glassfiber reinforced polyphthalamide for injection molding with strong mechanical properties especially at elevated temperatures, good long-term thermal stability and outstanding chemical resistance for highly stressed parts. This material has high toughness, stiffness, extremely low water absorption and outstanding dimensional stability. It features high flowability and allows filling of complex parts with thin wall thickness. It is easily processable with excellent melt stability.
黄卡号码：E41871-104037903
增强材料：玻璃纤维30%增强
材料特性：芳香、高刚性、高韧性、较高的熔体稳定性、良好的加工性能、流动性高、耐化学品良好、热稳定良好、吸水低或不吸水、High Dimensional Stability
材料用途：薄壁部件
加工方法：粒子注射成型
供货地区：欧洲、北美洲
中国代理：苏州希普能工程塑料
Ultramid® Advanced N3HG6 加工参数表
| 物理性能 | 额定值 | 单位制 | 测试方法 |
| 密度 | 1.37 | g/cm³ | ISO 1183 |
| 收缩率 | ISO 294-4 | ||
| 垂直 | 0.98 | % | |
| 流动 | 0.47 | % | |
| 吸水率(饱和,23℃) | 2.0 | % | ISO 62 |
| 机械性能 | 额定值 | 单位制 | 测试方法 |
| 拉伸模量(23℃) | 10500 | MPa | ISO 527-1 |
| 拉伸应力(断裂,23℃) | 190 | MPa | ISO 527-2 |
| 拉伸应变(断裂,23℃) | 2.5 | % | ISO 527-2 |
| 冲击性能 | 额定值 | 单位制 | 测试方法 |
| 简支梁缺口冲击强度 | ISO 179 | ||
| -30℃ | 9.0 | kJ/m² | |
| 23℃ | 9.0 | kJ/m² | |
| 简支梁无缺口冲击强度 | ISO 179 | ||
| -30℃ | 60 | kJ/m² | |
| 23℃ | 65 | kJ/m² | |
| 热性能 | 额定值 | 单位制 | 测试方法 |
| 载荷下热变形温度(1.8 MPa,未退火) | 270 | ℃ | ISO 75-2/A |
| 溶融温度（DSC） | 300 | ℃ | ISO 3146 |
| 注射 | 额定值 | 单位制 | |
| 干燥温度 - 热风干燥机 | 120 | ℃ | |
| 干燥时间 | 8.0 | hr | |
| 建议的最大水分含量 | 0.050 | % | |
| 加工（熔体）温度 | 320 到 340 | ℃ | |
| 模具温度 | 100 到 160 | ℃ | |